Vydyne® 21SPG1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hf3NDI_Vydyne-21SPG1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne 21SPG1 product description to come. Typical Applications/End Uses: To come |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 2.0 | -- | % | |
| Flow : 23°C, 2.00 mm | 2.0 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | |
| Outdoor Suitability | f2 | -- | UL 746C |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 85.0 | -- | °C | |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 85.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.750 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 26 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 5 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.710 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.710 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 3 | -- | ||
| 3.00 mm | PLC 2 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.710 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.710 mm | 850 | -- | °C | |
| 1.50 mm | 850 | -- | °C | |
| 3.00 mm | 850 | -- | °C | |
| Oxygen Index | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 70.0 | °C | |
| Drying Time | 1.0 to 3.0 | hr | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 285 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 285 to 300 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANTEX® 640E | Nantex Industry Co., Ltd. | NBR | NANTEX® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Altuglas® DRT MATT 101 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Sylvin 83012-90UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ ZL003 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |