OMIKRON XLT 50 NAT
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TECNOPOL |
| Trademark: | OMIKRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HeHVn5_OMIKRON-XLT-50-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP COPOLYMER, 20% TALCUM, NATURAL |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | > 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 9.00 - 11.0 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.500 - 1.00 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 206D | RTP Company | Nylon 612 | RTP |
| Tecopet® PT70 GR15 NL100 PS20 | Eurotec Engineering Plastics | PET | Tecopet® |
| Vipel® F701-BBB-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Geon™ Vinyl Wire & Cable WJKC304 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| LAMIGAMID® 510 | Schwartz Technical Plastic | PET | LAMIGAMID® |