LNP™ THERMOCOMP™ MX06403 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HeGyxF_LNP-THERMOCOMP-MX06403-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MX06403 is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized, UV Stabilized. Also known as: LNP* THERMOCOMP* Compound MF-1004 HS UV HP Product reorder name: MX06403 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.50 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 3100 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 66.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 290 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 140 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-210 | Teknor Apex Company | TPE | Medalist® |
| Sylvin 7833-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ASI POLYPROPYLENE 1188-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Karina IVORY PVC COMPOUND 70900-35/1-E-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen 4021 K RM Powder | LyondellBasell Industries | MDPE | Lupolen |