Sumikon® PM-6830
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite Co., Ltd. |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HdZSHf_Sumikon-PM-6830.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sumikon®PM-6830 is a phenolic (Phenolic) product,. It can be processed by injection molding and is available in North America or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.84 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.050 - 0.15 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 300 | °C | ISO 75-2/A |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 10 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.20 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Insulation Resistance, JIS K6911, as molded: 1E11 to 1E12 ohmInsulation Resistance, JIS K6911, after boiling: 1E10 to 1E11 ohmAppearance after heating, JIS K6911, @ 2 hrs: 200°CHDT A (1.80 MPa) Unannealed, ISO 75A-1,-2: >300°CAll ISO values were tested in accordance with JIS specifications. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Small Boss STPR004 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | SBS | Small Boss |
| IROGRAN® A 85 P 4380 | Huntsman Corporation | TPU-Polyether | IROGRAN® |
| LOTTMER SE-130AN | Lotte Chemical Corporation | SEBS | LOTTMER |
| Okirol® E-6F | DIOKI d.d. | PS (EPS) | Okirol® |
| ProPolymers PPA TI-50G | ProPolymers Inc. | PPA | ProPolymers |