NOVADURAN® 5810GN6-30
| Category: | PBT Alloy , Polybutylene Terephthalate Alloy |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | NOVADURAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HcXt1W_NOVADURAN-5810GN6-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVADURAN® 5810GN6-30 is a Polybutylene Terephthalate Alloy (PBT Alloy) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of NOVADURAN® 5810GN6-30 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 2.00 mm | 0.60 | % | |
| Flow : 2.00 mm | 0.30 | % | |
| Water Absorption (Saturation, 23°C) | 0.070 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 114 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 9700 | MPa | ISO 178 |
| Flexural Stress | 172 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 213 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 183 | °C | ISO 75-2/A |
| Melting Temperature | 224 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 50°C | 2.0E-5 | cm/cm/°C | |
| Flow : -30 to 120°C | 1.0E-5 | cm/cm/°C | |
| Flow : 50 to 120°C | 1.0E-5 | cm/cm/°C | |
| Transverse : -30 to 50°C | 8.0E-5 | cm/cm/°C | |
| Transverse : -30 to 120°C | 1.0E-4 | cm/cm/°C | |
| Transverse : 50 to 120°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.350 mm, BK | V-0 | ||
| 0.750 mm, All | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 255 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH5000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TAIRIPRO F4008 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Dugdale PVC Static Flexible PVC Nitrile Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Karina IVORY PVC COMPOUND 951-35/4-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS DG504X | AD majoris | PP, Unspecified | MAJORIS |