| 43% Glass Reinforced, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.49 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 7.6 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.2 | -- | % | |
| Viscosity Number | 120 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14000 | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 225 | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 14 | 16 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy (23°C) | 4.40 | -- | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 25 | -- | kV/mm | IEC 60243-1 |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.013 | -- | ||
| 1 MHz | 0.015 | -- | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Thermal Conductivity of Melt | 0.25 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 55200 | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Mowiol® 8-88 low ash | Kuraray Co., Ltd. | PVOH | Mowiol® |
| UNISOFT TPE™ ST-60A-BK-3-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| HANWHA LLDPE HS1600 | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| Lucalen A 2920 M | LyondellBasell Industries | LDPE | Lucalen |