TRISTAR® PC-10GFR-(V)
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | TRISTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hbh2CA_TRISTAR-PC-10GFR--V-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRISTAR® PC-10GFR-(V) is a Polycarbonate (PC) product filled with 10% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of TRISTAR® PC-10GFR-(V) include outdoor applications, electrical/electronic applications and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.17 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Outdoor Suitability | UL 746C | ||
| White | f2 | ||
| -- | f1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 15 | % | ASTM D1708 |
| Flexural Modulus (3.17 mm) | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 110 | J/m | ASTM D256 |
| Tensile Impact Strength (3.17 mm) | 53.3 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648 |
| RTI Elec | 80.0 to 125 | °C | UL 746 |
| RTI Imp | 80.0 to 115 | °C | UL 746 |
| RTI Str | 80.0 to 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C 1 | 6.0E+15 | ohms·cm | |
| 90°C 2 | 3.0E+15 | ohms·cm | |
| Dielectric Strength (3.00E-6 mm) | 19 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| 2.40 mm | 5VA | ||
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 875 | °C | IEC 60695-2-13 |
| Oxygen Index | 37 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 40 hr, 50% RH |
| 2 . | 96 hr, 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 X 131299 A | RTP Company | Nylon 66 | RTP |
| Next Nylon 66 Prime Series PG40-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| FRAGOM PR/112 UTW | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| INEOS LDPE 23H430 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| OP - PC - Filled PC B15-7SS | Oxford Polymers | PC | OP - PC - Filled |