Borealis PP RA130E
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HbGfEB_Borealis-PP-RA130E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RA130E is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is natural coloured. The product is used for single as well as for multilayer pipes, where you then differentiate between plastic multilayer and aluminium multilayer pipes. RA130E is intended to fulfill following standards and regulations, in case of appropriate industrial manufacturing standard procedures applied and a continuous quality system is implemented.
The pipe system will show high durability, no corrosion, good weldability, homogeneous joints, low tendency to incrustrations and fast and easy installation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 14 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 0°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | ISO 179/1eU |
| 0°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (0 to 70°C) | 1.5E-4 | cm/cm/°C | DIN 53752 |
| Thermal Conductivity | 0.24 | W/m/K | DIN 52612 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 210 | °C | |
| Cylinder Zone 2 Temp. | 180 - 210 | °C | |
| Cylinder Zone 3 Temp. | 180 - 210 | °C | |
| Cylinder Zone 4 Temp. | 180 - 210 | °C | |
| Cylinder Zone 5 Temp. | 180 - 210 | °C | |
| Melt Temperature | 220 | °C | |
| Die Temperature | 210 - 220 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 210 to 220°C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang W-8205N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| TOTAL Polyethylene LDPE LA 0710 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Zytel® PLUS PLS95G50DH2 BK261 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® PLUS |
| HAIPLEN EP100 MF3 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| SABIC® HDPE M453G | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |