VICTREX® PEEK 150CA30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hb9owK_VICTREX-PEEK-150CA30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black. Complex geometries with thin cross sections or long flow length where higher strength in a static or dynamic system is required. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Spiral Flow | 14.0 | cm | Internal method |
| Molding Shrinkage 1 | |||
| Vertical flow direction : 200°C | 0.50 | % | |
| Flow direction : 200°C | 0.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.040 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 26000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 260 | MPa | ISO 527-2 |
| Fracture, 125°C | 150 | MPa | ISO 527-2 |
| Fracture, 175°C | 95.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 24000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 360 | MPa | ISO 178 |
| 125°C | 250 | MPa | ISO 178 |
| 175°C | 120 | MPa | ISO 178 |
| 225°C | 60.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 300 | MPa | ISO 604 |
| 120°C | 200 | MPa | ISO 604 |
| 200°C | 70.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 7.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 339 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : < 143°C | 5.0E-6 | cm/cm/°C | ISO 11359-2 |
| Flow : > 143°C | 6.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1800 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.95 | W/m/K | Internal method |
| RTI Imp | 200 | °C | UL 746 |
| RTI | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 2(23°C) | 1.0E+5 | ohms·cm | ASTM D4496 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Toxicity | NES 713 | ||
| CO Content | 0.0500 | NES 713 | |
| CO2 Content | 0.120 | NES 713 | |
| Total Gases | 0.170 | NES 713 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 320 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 365 | °C | |
| Middle Temperature | 370 - 375 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 385 | °C | |
| Mold Temperature | 180 - 210 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | 385°C nozzle |
| 2 . | 1V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-G40 | Polymer Resources Ltd. | PBT | PRL |
| Nylene® 733 | Custom Resins Group | Nylon 6 | Nylene® |
| Ferro PP MPP20FU16BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Generic EnBA | Generic | EnBA | Generic |
| LNP™ LUBRICOMP™ IFL36R compound | SABIC Innovative Plastics Europe | Nylon 612 | LNP™ LUBRICOMP™ |