POLYLAN AG15A1 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/10.0 kg | 17 | g/10 min | |
| 200°C/5.0 kg | 1.6 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 110 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2650 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Flexural Strength (23°C) | 84.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 89.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 12.7 mm | 101 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 104 | °C | ISO 306/A, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502-A Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| TECHNYL® C 218 MZ20 V10 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| YUCLAIR® FT810P | SK Global Chemical | LLDPE | YUCLAIR® |
| AVP™ TLL80CU | SABIC Innovative Plastics | PC | AVP™ |
| Hifax CA 1110 G2 HF C11306 | LyondellBasell Industries | PP Copolymer | Hifax |