CYCOLAC™ BDT6500 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HZnIBW_CYCOLAC-BDT6500-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AUTOMOTIVE. Low gloss, color concentratable for interior applications. Natural only. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.3 | g/10 min | ASTM D1238 |
| Spiral Flow | 86.4 | cm | Internal Method |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2210 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 48.3 | MPa | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2410 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 42.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 93.9 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 81.1 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | |
| CLTE - Flow (-40 to 60°C) | 1.5E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 25 | ASTM D523 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1000 sec^-1) | 155 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 193 to 238 | °C | |
| Middle Temperature | 210 to 249 | °C | |
| Front Temperature | 221 to 254 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil MED4-4220 | NuSil Technology | Silicone | NuSil |
| Karina IVORY PVC COMPOUND 803-35/1-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TYC 2101N C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Dow Corning® MG-2402 | Dow Corning Corporation | Silicone | Dow Corning® |
| LEXAN™ HFD4412 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |