| Polyamide 6 natural, high impact grade |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.4 - 1.8 | % | ISO 294-4 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 8.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 1800 | MPa | ASTM D790 |
| Flexural Strength (Break) | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 50.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 160 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with ISO 2577.Limit Temperature, IEC 216, 20000 hrs: 55°CWater Absorption @ Equil. ASTM D570, 50% RH, 23 °C: 1.0 to 1.3% |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niretan A 27 EXL | Soredi S.p.a. | Nylon 66 | Niretan A |
| HiFill® PA6/6 GF33 LE BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Iupital® A25-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| LNP™ LUBRICOMP™ RBL36L compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| SABIC® LLDPE MG200024 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |