T & T Marketing TT 103FR
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | T & T Marketing, Inc. |
| Trademark: | T & T Marketing |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HZCX0s_T-T-Marketing-TT-103FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TT 103FR is a halogenated fire resistant high density polyolefin compound which offers an excellent balance of flame retardancy, processability, electrical and physical properties. TT 103FR is designed to reduce flame spread and achieve a VW-1 flame resistant rating on 14 AWG wires and larger. It also offers good extrusion processing characteristics on either conventional polyethylene or PVC extrusion lines. In addition, TT 103FR contains a UV stabilization additive package that provides effective long-term UV weather resistance. TT 103FR is readily pigmented to a variety of colors using standard wire and cable color concentrates designed for polyolefins. Application TT 103FR can be used as an insulating material for data grade multi-pair and solid coaxial cable constructions. TT 103FR can be used in certain cable designs to meet UL 1581, UL 444, CSA FT-4, UL 1666 specifications and IEEE 383 and CSA C22.2 No. 3 requirements for vertical flame tests. TT 103FR complies with "Restriction of Hazardous Substances" Directive, Citation 2002-95-EC, commonly known as RoHS without exemption and does not contain decabromodiphenyl oxide. TT 103FR provides good resistance to abrasion, impact and crush. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 17.2 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 600 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile strength retention- 7 days at 136°C (762.0 µm) | > 90 | % | UL 1581 |
| Elongation retention rate- 7 days at 136°C (762.0 µm) | > 90 | % | UL 1581 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 24:1 | ||
| Extruder Screw Compression Ratio | 2.7 to 3.5:1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (1.91 mm) | 1.6E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.91 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1.91 mm, 60 Hz) | 2.40 | ASTM D150 | |
| Dissipation Factor (1.91 mm, 60 Hz) | 2.7E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm) | V-0 | UL 94 | |
| Oxygen Index | 29 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 188 | °C | |
| Cylinder Zone 2 Temp. | 199 | °C | |
| Cylinder Zone 3 Temp. | 204 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 204 - 210 | °C |
| Extrusion instructions |
|---|
| Screw: Single FlightDie: Smooth transition, With >= 1/8 in. land, Die & Tip include angle: 22-35°Throat: Water-cooled |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STYRON™ 695 | Americas Styrenics LLC | PS (GPPS) | STYRON™ |
| ColorRx® PP2-1000RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| ESTACARB PC 2020 GF V0 HF | Cossa Polimeri S.r.l. | PC | ESTACARB |
| Karina BLACK PVC COMPOUND -E 855-48/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GRAY COLOR CONCENTRATE -E 18/ 89-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |