LNP™ THERMOCOMP™ PCAF04FRHH compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HZAekI_LNP-THERMOCOMP-PCAF04FRHH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP* THERMOCOMP* PCA04FRHH is a 20 % glass reinforced PC+ABS blend without chlorinated or brominated flame retardants. LNP* THERMOCOMP* complies with the material requirements as specified in TCO"99 and Blue Angel ecolabels. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 8.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.20 to 0.40 | % | |
| Across Flow | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 5800 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 23 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 100 mm Span) | 118 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 130 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.50 mm) | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 220 to 260 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Nozzle Temperature | 220 to 260 | °C | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6917 WT021 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| EPO-TEK® OE184 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| PENTAMID A GV30 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Sumikon® PM-6530 | SBHPP | Phenolic | Sumikon® |
| Sylvin 9790-60 Green 3205 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |