Ketron® PEEK 30% GF (EXTRUSION)
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Ketron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HYgYP4_Ketron-PEEK-30-GF-EXTRUSION-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extruded 30% Glass fiber reinforced polyetheretherketone. The addition of glass fibers significantly reduces the expansion rate and increases the flexural modulus of PEEK. This grade is ideal for structural applications that require improved strength, stiffness or stability, especially at temperatures above 300°F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | |
| Saturation | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 103 | ||
| R-Scale | 126 | ||
| Durometer Hardness (Shore D) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6890 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 159 | MPa | ASTM D790 |
| Compressive Modulus | 3790 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 152 | MPa | ASTM D695 |
| Shear Strength | 96.5 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 232 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 249 | °C | |
| Peak Crystallization Temperature (DSC) | 340 | °C | ASTM D3418 |
| CLTE - Flow 1(-40 to 149°C) | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.43 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 3 | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 68°F |
| 2 . | EOS/ESD S11.11 |
| 3 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 222 BLACK 1N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| TOTAL Polyethylene EVA 1040 VN 4 | TOTAL Refining & Chemicals | EVA | TOTAL Polyethylene |
| Weihai Hisea CPE135A | Weihai Hisea Plastic Rubber Co., LTD. | CPE | Weihai Hisea |
| POTICON NT46 | Otsuka Chemical Co., Ltd. | Nylon, Unspecified | POTICON |
| LNP™ THERMOCOMP™ LF004E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |