Adiprene® LFP 3940A

Category:	PUR-PC/PPDI , Polyurethane (Polycarbonate, PPDI)
Manufacturer:	Chemtura
Trademark:	Adiprene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HXmYTs_Adiprene-LFP-3940A.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ADIPRENE LFP 3940A is a PPDI-terminated polycarbonate prepolymer having very low free PPDI content (typical < 0.1%) for easier management of health and safety during handling. ADIPRENE LFP 3940A yields high performance 93-96 Shore A hardness elastomers when cured with VIBRACURE® A 250 or HQEE. The high performance features of ADIPRENE LFP 3940A are due to PPDI (p-phenylene diisocyanate), a special building block that imparts exceptional properties to cast polyurethane elastomers. The unique combination of properties exhibited by PPDI-based prepolymers is superior to those available from standard prepolymers based on TDI or MDI. Features of ADIPRENE LFP 3940A include: Low Free PPDI Content Excellent hydrolytic stability, oil stability and thermal stability Long Pour Life Excellent Dynamics Good Tensile/Tear Strength Excellent Resilience

Message

ADIPRENE LFP 3940A is a PPDI-terminated polycarbonate prepolymer having very low free PPDI content (typical < 0.1%) for easier management of health and safety during handling. ADIPRENE LFP 3940A yields high performance 93-96 Shore A hardness elastomers when cured with VIBRACURE® A 250 or HQEE.

The high performance features of ADIPRENE LFP 3940A are due to PPDI (p-phenylene diisocyanate), a special building block that imparts exceptional properties to cast polyurethane elastomers. The unique combination of properties exhibited by PPDI-based prepolymers is superior to those available from standard prepolymers based on TDI or MDI.

Features of ADIPRENE LFP 3940A include:

Low Free PPDI Content

Excellent hydrolytic stability, oil stability and thermal stability

Long Pour Life

Excellent Dynamics

Good Tensile/Tear Strength

Excellent Resilience

General Information
Features	Good Tear Strength Good Thermal Stability High Tensile Strength Hydrolytically Stable Resilient
Processing Method	Casting

Hardness	Nominal Value		Test Method
Durometer Hardness (Shore A)	94 to 96		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
100% Strain	10.9	MPa
300% Strain	17.9	MPa
Tensile Strength	52.4	MPa	ASTM D412
Tensile Elongation (Break)	550	%	ASTM D412
Tear Strength (Split)	26	kN/m	ASTM D470
Compression Set			ASTM D395B
70°C, 22 hr	33	%
100°C, 22 hr	55	%
Bayshore Resilience	50	%	ASTM D2632

Thermoset	Nominal Value	Unit
Pot Life	5.0	min
Demold Time	> 60	min
Post Cure Time (127°C)	16	hr

Additional Information	Nominal Value	Unit
Dynamic Properties
Storage Modulus : 30°C	3.25E+8	dynes/cm²
Storage Modulus : 150°C	2.60E+8	dynes/cm²
Tangent Delta : 30°C	0.0220
Tangent Delta : 150°C	0.0190

Resin Grade	Manufacturer	Category	Trademark
Razamid® A121U-51	Razin™ Engineering Plastics	Nylon 66	Razamid®
SEPAZ™ K445CTS	Mando Advanced Materials Co., Ltd.	PPS	SEPAZ™
ASACLEAN™ UX	ASACLEAN - Sun Plastech Inc.	Proprietary	ASACLEAN™
Kepamid® 2330GFH	Korea Engineering Plastics Co., Ltd	Nylon 66	Kepamid®
Polygen SC75D-BK	Shanghai Polygen Science and Technology Co., Ltd.	PPS	Polygen