ASTALAC™ ASA 314
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HXQ34I_ASTALAC-ASA-314.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ASA 314 is a high melt flow, high impact grade of ASA which is designed for applications requiring a combination of toughness, mouldability, rigidity and heat resistance. ASA grades show superior colour and property retention compared to ABS and are typically used in applications such as exterior components requiring improved weatherability. Note: The letters "UV" or "W" indicate additional UV stabilisation [ ie: ASTALAC™ ASA 314UV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 70 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2200 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 67.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 430 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 25.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 77.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 88.0 | °C | |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 205 to 225 | °C | |
| Middle Temperature | 215 to 235 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 LF TFE 5 | RTP Company | PEEK | RTP |
| Stat-Rite® M690 | Lubrizol Advanced Materials, Inc. | PETG | Stat-Rite® |
| Ferro PP TPP20AJ46BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Fluran F-5500-A | Saint Gobain - Norton | Fluorelastomer | Fluran |
| OTECH PVC OM5017-Molding | OTECH Corporation | PVC, Unspecified | OTECH PVC |