KOPLA PA6 KRE1010
| Category: | Nylon 6+ABS , Polyamide 6 + ABS |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HX3Lo7_KOPLA-PA6-KRE1010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA6 KRE1010 is a Polyamide 6 + ABS (Nylon 6+ABS) material. It is available in Asia Pacific. Important attributes of KOPLA PA6 KRE1010 are:
Typical application of KOPLA PA6 KRE1010: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 to 2.4 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 52.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1670 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 460 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 170 | °C | |
| 1.8 MPa, Unannealed | 50.0 | °C | |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 4020-80AFR-XXXX | Vi-Chem Corporation | TPE | Sevrene® |
| NYLOY® NS-0100B-1 | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Elastollan® 1185 A HFFR | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| ICORENE® PP CO14RM | ICO Polymers SA, A Division of A. Schulman | PP Copolymer | ICORENE® |
| Sylvin 9915-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |