TRANSMARE® 14CT20-0.002
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HWeWQd_TRANSMARE-14CT20-0-002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 14CT20-0.002 is a 20% standard (gray) talc filled polypropylene copolymer for injection molding purposes with high impact and good flow. Not suitable for light colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 15 | g/10 min | |
| 230°C/5.0 kg | 60 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 21.0 | MPa | |
| Break, 4.00 mm | 16.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 3.5 | % | |
| Break, 4.00 mm | 50 | % | |
| Flexural Modulus 1 | 2000 | MPa | ISO 178 |
| Flexural Stress 2 | 33.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 2.5 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| 0°C | 5.7 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 3.5 | kJ/m² | |
| -20°C | 4.5 | kJ/m² | |
| 0°C | 6.5 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 143 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® H110MS | Reliance Industries Limited | PP, Unspecified | REPOL® |
| UBE Nylon 1013NW8 | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| Andur 95 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Kynar® 741 | Arkema | PVDF | Kynar® |
| PALMID® R 6 S GF 15 | pal plast GmbH | Nylon 6 | PALMID® |