DOWLEX™ 2085G
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HWCefN_DOWLEX-2085G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX* 2085G Polyethylene Resin is an ethylene-octene copolymer designed for general purpose thin gauge film applications. It is perfect for high strength consumer trash bags/liners. This product can be used in other applications that require toughness and also offers good melt strength for high throughput rates. Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 3.95 | J | Internal method |
| Film Puncture Force | 53.4 | N | Internal method |
| Film Puncture Resistance | 20.7 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 70.3 | J/cm³ | ASTM D882 |
| TD | 82.7 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 172 | MPa | ASTM D882 |
| 2% secant, MD | 152 | MPa | ASTM D882 |
| 1% secant, TD | 179 | MPa | ASTM D882 |
| 2% secant, TD | 159 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 8.27 | MPa | ASTM D882 |
| TD : Yield | 8.96 | MPa | ASTM D882 |
| MD : Fracture | 34.5 | MPa | ASTM D882 |
| TD : Fracture | 27.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 450 | % | ASTM D882 |
| TD : Fracture | 600 | % | ASTM D882 |
| Dart Drop Impact | 800 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 350 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 30 | ASTM D2457 | |
| Haze | 23 | % | ASTM D1003 |
| Additional Information |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5 in. (63.5 mm) 30:1 L/D/Size Screw Type: DSB II Die Gap: 70 mil (1.75 mm) Melt Temperature: 420°F Output: 12 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5:1 Screw Speed: 40 rpm Frost Line Height: 39 in. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flexalloy® 9600-72 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Gallonprene® GP320-55 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kepamid® 1320GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| ISPLEN® PB 150 G1F | REPSOL | PP Impact Copolymer | ISPLEN® |
| Plenco 08225 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |