NAS® 30
| Category: | Acrylic (SMMA) , Styrene Methyl Methacrylate Acrylic Copolymer |
| Manufacturer: | Styrolution |
| Trademark: | NAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HVZ0WU_NAS-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NAS 30 is a styrene acrylic copolymer that can be used in a variety of applications demanding a strong, stiff water-clear plastic resin with excellent thermal stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.2 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.60 | % | ASTM D955 |
| -- | 0.20 to 0.60 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation, 23°C | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 75 | ASTM D785 | |
| Ball Indentation Hardness | 169 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 3240 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 60.7 | MPa | ASTM D638 |
| Yield, 23°C | 60.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.3 | % | ASTM D638 |
| Break, 23°C | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3170 | MPa | ASTM D790 |
| -- | 3400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 101 | MPa | ASTM D790 |
| -- | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 21 | J/m | ASTM D256 |
| 23°C | 2.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ASTM D1525 1 |
| -- | 98.0 | °C | ISO 306/B50 |
| Maximum Service Temperature | 260 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 2 | 1.560 | ASTM D542, ISO 489 | |
| Transmittance (550 nm) | 91.4 | % | ASTM D1003 |
| Haze | 0.30 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 210 to 240 | °C | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | Sodium D Line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STAR-THERM® E A-2C | EPIC Polymers | Nylon 66 | STAR-THERM® |
| Evermore PUR SS-1065N | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Electrafil® PC 04009 FR BK | Techmer Engineered Solutions | PC | Electrafil® |
| Lupol® HI5205R | LG Chem Ltd. | TPO | Lupol® |
| Loyblend® TA-1810FR | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |