Lucky Enpla LPC1001F 9306
| Category: | PC , Polycarbonate |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HURyMd_Lucky-Enpla-LPC1001F-9306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LPC1001F 9306 is a polycarbonate (PC) product,. It is available in North America, Europe or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 - 0.65 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 53.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2280 | MPa | ASTM D790 |
| Flexural Strength 3 | 82.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 122 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 305 | °C | |
| Nozzle Temperature | 295 - 315 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Back Pressure | 0.490 - 2.94 | MPa | |
| Screw Speed | 30 - 50 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 280-300°CInjection Pressure (1st Pressure): 700-1200 kg/cm²Injection Pressure (2nd Pressure): 500-900 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKAEXCEL® PES 3600G | Sumitomo Chemical Co., Ltd. | PESU | SUMIKAEXCEL® PES |
| TAROPRENE® 1 A65 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| EMLON® 66 GBR 30 | EMAS Plastik San.Tic.AS. | Nylon 66 | EMLON® |
| Karina PINK COLOR CONCENTRATE -E 39/ 87-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Machine Cast MC-172 A/B | BJB Enterprises, Inc. | TSU | Machine Cast |