ULTEM™ AUT195 resin
| Category: | PEI+PCE , Polyether Imide + PCE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HU0zXl_ULTEMAUT195resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (340°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Across Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.90 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1 |
| Tensile Strength 2(Yield) | 96.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 70 | % | ASTM D638 |
| Flexural Modulus 4 | 3100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 6 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 195 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 180 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 195 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 80.0 - 100 | °C | |
| Rear Temperature | 320 - 340 | °C | |
| Middle Temperature | 330 - 350 | °C | |
| Front Temperature | 340 - 360 | °C | |
| Nozzle Temperature | 340 - 360 | °C | |
| Processing (Melt) Temp | 340 - 380 | °C | |
| Mold Temperature | 125 - 140 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 80*10*4 sp=62mm |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 GR25 NL XA60 | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Taitalac® 6000F | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| VINIKA® D6188 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| Nypol® PA A3 G25 HS UV RH HF PRTA011 NR435 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Hoffman PVC V7-47 | Hoffman Plastic Compounds Inc. | PVC, Rigid | Hoffman PVC |