High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard viscosity, FDA food contact compliant, colour black. Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.51 | g/cm³ | ISO 1183 |
| Spiral Flow 2 | Internal method | ||
| -- 3 | 8.50 | cm | Internal method |
| -- 4 | 41.0 | cm | Internal method |
| Molding Shrinkage 5 | ISO 294-4 | ||
| Vertical flow direction : 190°C | 0.90 | % | ISO 294-4 |
| Flow direction : 190°C | 0.30 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.040 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 170 | MPa | ISO 527-2 |
| Fracture, 125°C | 120 | MPa | ISO 527-2 |
| Fracture, 175°C | 60.0 | MPa | ISO 527-2 |
| Fracture, 225°C | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 260 | MPa | ISO 178 |
| 125°C | 190 | MPa | ISO 178 |
| 175°C | 80.0 | MPa | ISO 178 |
| 225°C | 50.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 250 | MPa | ISO 604 |
| 120°C | 160 | MPa | ISO 604 |
| 200°C | 55.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 328 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : > 143°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : < 143°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1700 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.30 | W/m/K | ISO 22007-4 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 220 | °C | UL 746 |
| RTI | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C, 1 kHz) | 3.30 | IEC 60250 | |
| Dissipation Factor (23°C, 1 MHz) | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 560 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 360 | °C | |
| Middle Temperature | 370 - 375 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 385 | °C | |
| Mold Temperature | 180 - 200 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Crystalline |
| 2 . | Mold temperature: 190°C, melt temperature: 385°C |
| 3 . | 1 mm |
| 4 . | 3 mm |
| 5 . | 385°C nozzle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT SG3251 | Sincerity Australia Pty Ltd. | PBT+PET | Sindustris PBT |
| Talcoprene® 540TL2 LE NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Delta PBR-1G30 | Delta Polymers | PBT | Delta |
| Fainplast PVC MPH 57/Y | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| SQUARE® LSR6010-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |