Vydyne® R533T
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HTLzUq_Vydyne-R533T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R533T is a translucent 33% glass-fiber reinforced PA66 resin designed specifically for use in power-steering reservoirs and other applications where chemical resistance, whiteness and transmittance are required. Vydyne R533T resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts. Typical Applications/End Uses: To come |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.80 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10200 | 7900 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 210 | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 4.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9500 | 6500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 290 | 205 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 8.0 | 12 | kJ/m² | |
| 23°C | 12 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | No Break | 85 kJ/m² | ||
| 23°C | No Break | 90 kJ/m² | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 10 | 12 | kJ/m² | |
| 23°C | 12 | 14 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 252 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature | 264 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 2.2E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C |
| Optical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Transmittance | 23.0 | -- | % | ASTM D1003 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7500 GF 20 GK 10 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Zytel® FG42A NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Next Nylon 66 Industrial Series PX-02ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Industrial Series |
| Lushan EP252 | Guangzhou Lushan New Materials Co., Ltd | PE, Unspecified | Lushan |
| OTECH PVC OM6525-Boot | OTECH Corporation | PVC, Unspecified | OTECH PVC |