Starpylen MFM43S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HTLcBH_Starpylen-MFM43S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen MFM43S is a Mineral Filled, Glass Fiber Reinforced, Polypropylene Injection Molding Resin, also recognised as Starpylen WV 30VMC S37/7 Black 301 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.20 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 56.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 86.0 | MPa | |
| -- 4 | 45.0 | MPa | |
| Flexural Strain at Break 5 | 3.7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(1.8 MPa, Unannealed, 64.0 mm Span) | 124 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.4E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.3E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 215 to 225 | °C | |
| Front Temperature | 225 to 250 | °C | |
| Processing (Melt) Temp | 225 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PMMA 5805 SZ | TER HELL PLASTIC GMBH | Acrylic (PMMA) | TEREZ PMMA |
| Ultraform® H 4320 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Ad-Tech Urethanes UC-4521 | Ad-Tech Plastic Systems Corp. | TSU | Ad-Tech Urethanes |
| Daelim Po1y® LH-5540 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| ESTADIENE 1030 V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |