LNP™ THERMOCOMP™ IF006 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HSVphr_.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* IF006 is a compound based on nylon 6/12 resin containing glass fibre Also known as: LNP* THERMOCOMP* Compound IF-1006 Product reorder name: IF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6050 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 4.2 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 209 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 188 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.6E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 254 - 266 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 271 - 277 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 350A4861313 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Celstran® PP-GF30-0553 Black | Celanese Corporation | PP Copolymer | Celstran® |
| Hostaform® C 27021 XAP² ™ LS colored | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| MAJORIS CG308X - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 9077-90 Grey 9450 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |