Thermec™ 4150CF40
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Thermec™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HRc89c_Thermec-4150CF40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermec™4150CF40 is a polyphenylene sulfide (PPS) material, which contains a 40% carbon fiber reinforced material. This product is available in North America and is processed by injection molding. Thermec™The main characteristics of 4150CF40 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 207 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 29000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 276 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 268 | °C | ASTM D648 |
| Melting Temperature | 280 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Volum Resistivity, ASTM D257: <1e5 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 - 149 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 316 - 343 | °C | |
| Mold Temperature | 135 - 149 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.689 | MPa | |
| Screw Speed | 100 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 6.35 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PP 2131 70/35 | MBA Polymers | PP Copolymer | MBA PP |
| S&E Battery GPP1001V0M-HCO-15 | S&E Specialty Polymers, LLC | TPO | S&E Battery |
| Sasol Polymers PP HNR100 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Karina BLUE PVC COMPOUND 830-06/291-IS-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 830 01 HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |