TRANSMARE® 14CNF30-0.001
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HRT5M8_TRANSMARE-14CNF30-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 14CNF30-0.001 is a 30% bamboo fibre reinforced polypropylene copolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 2800 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 31.0 | MPa | |
| Break, 4.00 mm | 31.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 3.3 | % | |
| Break, 4.00 mm | 4.7 | % | |
| Flexural Modulus 1 | 2950 | MPa | ISO 178 |
| Flexural Stress 2 | 47.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -20°C | 3.7 | kJ/m² | |
| 0°C | 4.7 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 4.3 | kJ/m² | |
| 0°C | 5.6 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 157 | °C | ISO 306/A50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 | °C | |
| Middle Temperature | 175 | °C | |
| Front Temperature | 185 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2263 | RTP Company | PEEK | RTP |
| Evatane® 28-40 | Arkema | EVA | Evatane® |
| K-Prene INSULATION EPR 5088 | Technovinyl Polymers India Ltd. | MPR | K-Prene |
| Karina IVORY PVC COMPOUND -E 552D35/ 1-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLEXIGLAS® Sheet Optical (RP) | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |