ULTEM™ ATX3562R resin
| Category: | PEI+PCE , Polyether Imide + PCE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HQugAm_ULTEM-ATX3562R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.10 | % | |
| Equilibrium, 23°C, 50% RH | 0.040 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14900 | MPa | ASTM D638 |
| -- | 14700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 125 | MPa | ASTM D638 |
| Yield | 121 | MPa | ISO 527-2/5 |
| Break 3 | 125 | MPa | ASTM D638 |
| Break | 121 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.5 | % | ASTM D638 |
| Yield | 1.4 | % | ISO 527-2/5 |
| Break 5 | 2.5 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 12900 | MPa | ASTM D790 |
| -- 7 | 13600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 172 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 4.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 50 | J/m | ASTM D256 |
| 23°C | 50 | J/m | ASTM D256 |
| -30°C 10 | 5.4 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 12(23°C) | 5.6 | kJ/m² | ISO 180/1U |
| Reverse Notch Izod Impact (3.20 mm) | 110 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 12.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 13 | 195 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 183 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 182 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 184 | °C | ASTM D1525 15 |
| -- | 187 | °C | ISO 306/B50 |
| -- | 195 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 150°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 1.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 3.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.1E+15 | ohms | ASTM D257 |
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 338 to 360 | °C | |
| Middle Temperature | 343 to 366 | °C | |
| Front Temperature | 349 to 371 | °C | |
| Nozzle Temperature | 349 to 371 | °C | |
| Processing (Melt) Temp | 349 to 371 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axpoly® r-PP51 1047 | Axion Polymers | PP Copolymer | Axpoly® |
| Chemlon® 140 BH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| HOPELEX PCN-2004 | Lotte Chemical Corporation | PC | HOPELEX |
| Hyundai EP Matt MF502H/Natural | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Matt |
| Edistir® N 3380 | Versalis S.p.A. | PS (GPPS) | Edistir® |