Ebalta AH 110 / TL
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HQNZHh_Ebalta-AH-110-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta AH 110 is an unfilled epoxy resin with high strength values and dimensional stability, even at increased temperature. It can be used as casting resin with powdered fillers as aluminium powder, laminating resin with glass fabric and binder with grainy fillers as aluminium granules. Depending on application the suitable hardener can be mixed with the resin. AH 110/TL is suitable as binder and backfilling resin up to 100°C. For laminates post-curing is essential, if possible before demoulding. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 83 to 89 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3100 to 3700 | MPa | ISO 178 |
| Flexural Stress | 130 to 150 | MPa | ISO 178 |
| Compressive Stress | 105 to 125 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 26 to 46 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 97.0 to 103 | °C | ISO 75-2/B |
| Glass Transition Temperature | 110 | °C | DSC |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 24 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time | |||
| 60°C | 6.0 to 8.0 | hr | |
| 90°C | 3.0 to 5.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.11 to 1.15 | g/cm³ | |
| Viscosity (25°C) | 1.2 to 1.6 | Pa·s | |
| Curing Time (20°C) | 24 to 28 | hr | |
| Pot Life 1(20°C) | 85 to 95 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP673G | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Verolloy B5524 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| Next Nylon 66 Prime Series PG15-01BL | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Chiao Fu PA66 MD312G43 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| ALCOM® PA66 910/1.3 CF/GF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |