Celstran® PA66-GF60-02-Natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HPs4ik_Celstran-PA66-GF60-02-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 60% long glass fiber reinforced, heat stabilized, Nylon 6/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.050 - 0.10 | % | ASTM D955 |
| Transverse flow | 0.10 - 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 20800 | MPa | ASTM D638 |
| 23°C | 23200 | MPa | ASTM D638 |
| 121°C | 13300 | MPa | ASTM D638 |
| -- | 21600 | MPa | ISO 527-2/1A/1 |
| 80°C | 11900 | MPa | ISO 527-2/1A |
| Tensile Strength | |||
| Fracture, -40°C | 354 | MPa | ASTM D638 |
| Fracture, 23°C | 318 | MPa | ASTM D638 |
| Fracture, 121°C | 173 | MPa | ASTM D638 |
| Fracture | 280 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 1.9 | % | ASTM D638 |
| Fracture, 23°C | 1.8 | % | ASTM D638 |
| Fracture, 121°C | 2.2 | % | ASTM D638 |
| Fracture | 1.7 | % | ISO 527-2/1A/5 |
| Fracture, 80°C | 2.0 | % | ISO 527-2/1A |
| Flexural Modulus (23°C) | 19400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 460 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 54 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 263 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 285 - 295 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 300 - 310 | °C | |
| Nozzle Temperature | 300 - 315 | °C | |
| Processing (Melt) Temp | 300 - 315 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 300 to 315°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNFROST® KD60HA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Trexprene® A88CW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| DynaPath™ C2045CFT | Polymer Dynamix | Nylon 66 | DynaPath™ |
| EPO-TEK® P1011S | Epoxy Technology Inc. | PI, TS | EPO-TEK® |
| Pebax® 4033 SP 01 | Arkema | PEBA-Ether | Pebax® |