RIALENE® P 100 SGF30 ST F V-0 natural

Category:	PP, Unspecified , Polypropylene
Manufacturer:	RIA-Polymers GmbH
Trademark:	RIALENE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HPcXiZ_RIALENE-P-100-SGF30-ST-F-V-0-natural.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

RIALENE P 100 SGF30 ST F V-0 natural is a semi-crystalline thermoplastic construction material based on polypropylene (PP), reinforced with 30 % special glass fiber (SGF) which is optimized linked to the polymer matrix.

RIALENE P 100 SGF30 ST F V-0 natural will be processed by injection molding and has halogen- and heavy metal-free fire protection equipment.

RIALENE P 100 SGF30 ST F V-0 natural is characterized by the following properties:

UL 94 V-0 listed at 1.5 mm

Conform to GWIT 800 °C at 1.5 mm

excellent rigidity and strength with good elongation behavior

excellent thermo-mechanical properties

halogen- and heavy metal-free flame retardants (conform to WEEE and RoHS)

very low smoke density

no corrosion during processing

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	Flame retardancy
Features	Semicrystallization Rigidity, high High strength Halogen-free Flame retardancy
Agency Ratings	EU 2002/96/EC (WEEE)
RoHS Compliance	RoHS compliance
Appearance	Natural color
Processing Method	Injection molding
Resin ID (ISO 1043)	PP SGF30

Physical	Nominal Value	Unit	Test Method
Density	1.33	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)	4.30	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction	0.30 - 0.50	%	ISO 294-4
Flow direction	0.20 - 0.30	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	8750	MPa	ISO 527-2/1
Tensile Stress			ISO 527-2/5
Yield	95.0	MPa	ISO 527-2/5
Fracture	94.0	MPa	ISO 527-2/5
Tensile Strain			ISO 527-2/5
Yield	3.6	%	ISO 527-2/5
Fracture	3.9	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	11	kJ/m²	ISO 179/1eA
23°C	11	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	48	kJ/m²	ISO 179/1eU
23°C	49	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	160	°C	ISO 75-2/B
1.8 MPa, not annealed	151	°C	ISO 75-2/A
Vicat Softening Temperature	145	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity	> 1.0E+17	ohms·cm	IEC 60093
Dielectric Strength	41	kV/mm	IEC 60243-1
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.750 mm	V-2		UL 94
1.50 mm	V-0		UL 94
3.00 mm	V-0		UL 94
Glow Wire Flammability Index (1.50 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (1.50 mm)	800	°C	IEC 60695-2-13

Additional Information
Mechanical values determined after storage > 16 h at standard conditioning atmosphere (23 °C / 50 % rel. h.)

Injection	Nominal Value	Unit
Drying Temperature	95.0	°C
Drying Time	3.0	hr
Suggested Max Moisture	0.030	%
Hopper Temperature	50.0 - 70.0	°C
Rear Temperature	220 - 230	°C
Middle Temperature	220 - 240	°C
Front Temperature	220 - 250	°C
Nozzle Temperature	220 - 250	°C
Processing (Melt) Temp	220 - 250	°C
Mold Temperature	40.0 - 60.0	°C
Injection Rate	Slow-Moderate
Back Pressure	0.500 - 5.00	MPa

Resin Grade	Manufacturer	Category	Trademark
RAYPRENE® NB223-S4005	R&P (Pte.) Ltd.	TPE	RAYPRENE®
ColorRx® PE2-0200RX	LTL Color Compounders, Inc.	HDPE	ColorRx®
Colorite G Series 7512G-015	Colorite Polymers	PVC, Flexible	Colorite G Series
HiFill® PP TM20 FR NAT	Techmer Engineered Solutions	PP, Unspecified	HiFill®
Plaslube® PA6/12 01430	Techmer Engineered Solutions	Nylon 12	Plaslube®