ELITE™ 5940G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HPIlbH_ELITE-5940G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™ 5940G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. Main Characteristics:
Complies with
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 1.92 | J | |
| Film Puncture Force | 44.5 | N | |
| Film Puncture Resistance | 9.51 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 108 | J/cm³ | ASTM D882 |
| TD | 124 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 625 | MPa | ASTM D882 |
| 2% secant, MD | 503 | MPa | ASTM D882 |
| 1% secant, TD | 758 | MPa | ASTM D882 |
| 2% secant, TD | 607 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 20.7 | MPa | ASTM D882 |
| TD : Yield | 24.1 | MPa | ASTM D882 |
| MD : Fracture | 35.9 | MPa | ASTM D882 |
| TD : Fracture | 32.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 460 | % | ASTM D882 |
| TD : Fracture | 640 | % | ASTM D882 |
| Dart Drop Impact | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 40 | g | ASTM D1922 |
| TD | 650 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 126 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 20 | ASTM D2457 | |
| Haze | 30 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：35英寸 螺杆类型：DSB II 模具间隙：70密耳（1.7毫米）。 熔化温度：395华氏度 产量：10磅/小时/英寸（模具周长） 模具直径：8英寸 |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PBT EB225 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| Vyncolit® BXE6952 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Amilan® U320 | Toray Resin Company | Nylon 66 | Amilan® |
| Chiao Fu PA66 MD312LST BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| LEXAN™ BPL1000 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |