DuraGrip® DGR 6070BK
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Advanced Polymer Alloys |
| Trademark: | DuraGrip® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HOWGkF_DuraGrip-DGR-6070BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DuraGrip® 6070BK is a general purpose Thermoplastic Elastomer (TPE) designed for injection molding and extrusion processes. It has a high coefficient of friction, low melt viscosity and bonds well to polypropylene. DuraGrip® 6070BK is not hygroscopic and under normal conditions does not require drying. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.985 | g/cm³ | ASTM D792 |
| -- | 0.983 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 1.59mm | 2.1 | % | ASTM D955 |
| Flow : 3.18mm | 1.3 | % | ASTM D955 |
| Transverse flow : 1.59mm | 1.1 | % | ASTM D955 |
| Transverse flow : 3.18mm | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 72 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| 100% strain | 2.62 | MPa | ASTM D412, ISO 37 |
| 300% strain | 3.43 | MPa | ASTM D412, ISO 37 |
| Tensile Strength (Yield) | 8.34 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation (Break) | 640 | % | ASTM D412, ISO 37 |
| Tear Strength 1 | 28.5 | kN/m | ASTM D624 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (190°C, 294 sec^-1) | 130 | Pa·s | ASTM D3835 |
| Additional Information |
|---|
| The value listed as Density -Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.The value listed as Density, ISO 1183, was tested in accordance with ISO 2781. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 188 - 199 | °C | |
| Middle Temperature | 199 - 210 | °C | |
| Front Temperature | 216 - 227 | °C | |
| Nozzle Temperature | 204 - 221 | °C | |
| Processing (Melt) Temp | 199 - 221 | °C | |
| Mold Temperature | 43.3 - 54.4 | °C | |
| Injection Pressure | 1.03 - 4.14 | MPa | |
| Screw Speed | 25 - 100 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 to 3 in³/secInjection Time (1st Stage/Boost): 0.5 to 4 secSecond Stage Pressure: 150 to 300 psiSecond Stage Time: 3 to 10 secCooling Time: 10 to 20 secBack Pressure: 20 to 75 % |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 FR UV | RTP Company | PBT | RTP |
| Telcar® TL-2717B | Teknor Apex Company | TPE | Telcar® |
| EVALENE® PP PHJ1502 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| FORMULA P COMP 5220 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Plenco 04485 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |