DOWLEX™ 2070G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HOCXpE_DOWLEX-2070G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | Internal method | ||
| 20 µm | 8.69 | J/cm³ | Internal method |
| 51 µm | 5.79 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 20 µm | 76.4 | J/cm³ | ASTM D882 |
| MD : 51 µm | 99.0 | J/cm³ | ASTM D882 |
| TD : 20 µm | 89.9 | J/cm³ | ASTM D882 |
| TD : 51 µm | 97.1 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 20 µm | 183 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 192 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 211 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 228 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 10.7 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 10.5 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 11.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.6 | MPa | ASTM D882 |
| MD : Break, 20 µm | 38.0 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 35.6 | MPa | ASTM D882 |
| TD : Break, 20 µm | 28.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 29.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 440 | % | ASTM D882 |
| MD : Fracture, 51 µm | 620 | % | ASTM D882 |
| TD : Break, 20 µm | 650 | % | ASTM D882 |
| TD : Fracture, 51 µm | 680 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709A | ||
| 20 µm | 150 | g | ASTM D1709A |
| 51 µm | 310 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 250 | g | ASTM D1922 |
| MD : 51 µm | 810 | g | ASTM D1922 |
| TD : 20 µm | 690 | g | ASTM D1922 |
| TD : 51 µm | 1200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 20.3 µm | 56 | ASTM D2457 | |
| 45°, 50.8 µm | 65 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 20.3 µm | 11 | % | ASTM D1003 |
| 50.8 µm | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 218 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：MC-4 阻隔 模具间隙：40 密尔 (1 mm) 熔体温度：425°F (218°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：85 rpm 冷冻线高度：20 英寸 (508 mm) 脱离速度：0.8 密尔为 190 fpm，2.0 密尔为 80 fpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® PUG 10 | API SpA | SEBS | megol® |
| ALTECH® PP-H B 4930/506 MR30 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| AMTOPP VA25 | Inteplast Group | PP, Unspecified | AMTOPP |
| Cellophane™ 400P25 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| KumhoSunny PBT HEB4010 | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |