Baynat® 3002

Category:	PUR-Ether/MDI , Polyurethane (Polyether, MDI)
Manufacturer:	Covestro - PUR
Trademark:	Baynat®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HO9Qgb_Baynat-3002.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Baynat 3002 polyurethane foam system is used in automotive headliner applications. The Baynat 3002 polyurethane system is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (MDI). Component B is a polyether polyol system. Baynat 3002 polyurethane foam system is used in automotive headliner applications. This system allows low weight, good thermal dimensional stability, and high definition of surface structure. As with any product, use of the Baynat 3002 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

General Information
Features	Good dimensional stability Thermal stability, good
Uses	Foam Application in Automobile Field Car interior parts
Forms	Liquid

Physical	Nominal Value	Unit	Test Method
Density	0.0300	g/cm³	ASTM D3574A

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2.78	MPa
Tensile Strength	0.269	MPa	ASTM D3575

Elastomers	Nominal Value	Unit	Test Method
Tear Strength ¹	0.893	kN/m	ASTM D624
Compression Set ²	14	%

Thermoset	Nominal Value
Thermoset Components
Component a	按重量计算的混合比: 160 - 170
Component B	Mixing ratio by weight: 100

Additional Information
Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity at 25°C: 1.24 Flash Point PMCC: >93°C Bulk Density at 25°C: 10.3 lb/gal Part B Type: Polyol Blend Appearance: Pale Yellow Liquid Specific Gravity at 25°C: 1.045 Flash Point PMCC: 122°C Bulk Density at 25°C: 9.01 lb/gal Processing Parameters: Chemical Temperature: 20 to 22°C Material Pressures: 13 to 20 bar Stirrer Speed: 1800 to 2000 rpm Lid Usage: No Lid

Additional Information

Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity at 25°C: 1.24 Flash Point PMCC: >93°C Bulk Density at 25°C: 10.3 lb/gal Part B Type: Polyol Blend Appearance: Pale Yellow Liquid Specific Gravity at 25°C: 1.045 Flash Point PMCC: 122°C Bulk Density at 25°C: 9.01 lb/gal Processing Parameters: Chemical Temperature: 20 to 22°C Material Pressures: 13 to 20 bar Stirrer Speed: 1800 to 2000 rpm Lid Usage: No Lid

Note Message
1 .	C mould
2 .	50%

Resin Grade	Manufacturer	Category	Trademark
COPYLENE® CH005	Phillips 66	PP Homopolymer	COPYLENE®
RTP 2599 X 130537 AC-705695 LIGHT BLUE	RTP Company	PC+ABS	RTP
apilon 52® D1 45	API SpA	TPU-Polyester	apilon 52®
OTECH ALLOY OTO9150LSZH - Riser Jacket	OTECH Corporation	TP, Unspecified	OTECH ALLOY
ForTii® XS51	DSM Engineering Plastics	Nylon 4T	ForTii®