Ultralloy™ 304
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Ultralloy™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HNSBI3_Ultralloy-304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The ULTRALLOY series of liquid molding compounds are tough, fast cycling, low cost, and easy to use. ULTRALLOY is designed to be used with Liquid Molding, open casting, pressure casting, or vacuum casting processes. ULTRALLOY can be used with silicone, epoxy, urethane, polyester, or aluminum molds. Low cost molds and fast cycle times are two key attributes of ULTRALLOY. ULTRALLOY is available in several series. Each series has different products with different physical properties. Properties such as elongation, tensile strength, and modulus of elasticity can be selected to mold parts with the correct physical characteristics. Choose the ULTRALLOY material with the exact properties you need, or that are required to meet specifications. ULTRALLOY is available in opaque white, clear/transparent, and in fire retardant (UL 94V-0) versions. Custom coloring can be achieved by pigmenting ULTRALLOY with Hapco's easy to mix color dispersions. Both opaque and translucent color dispersions are available. ULTRALLOY can be molded in inexpensive molds, reducing total part cost, for short run programs. ULTRALLOY is made for prototypes and short runs of plastic parts. ULTRALLOY fills the need for low cost, high performance parts, in volumes less than 10,000 parts per year. ULTRALLOY 300 SERIES A series of clear, flame retardant (UL94 V-O), Liquid Molding Compounds. These products have a hardness of 85D and are fairly stiff with a flexural strength of over 13,000 psi. These materials are easily pigmented and available in gel times ranging from 8.5 to 60 minutes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 14 | g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 25.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1540 | MPa | ASTM D638 |
| Tensile Strength | 73.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 2520 | MPa | ASTM D790 |
| Flexural Strength | 95.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Unnotched Izod Impact | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 110 | ||
| Thermoset Mix Viscosity 2(25°C) | 250 to 350 | cP | ASTM D4878 |
| Demold Time (21°C) | 300 to 480 | min | Internal Method |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Range: 250 to 350 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 H TFE 5 | RTP Company | Nylon 66 | RTP |
| Santron IMS2007LF | Bhansali Engineering Polymers Limited | SAN | Santron |
| Unichem 8634 | Colorite Polymers | PVC, Unspecified | Unichem |
| DURANEX® 3300H | Polyplastics Co., Ltd. | PBT | DURANEX® |
| ELASTOSIL® R plus 4846/30 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |