OxyShield® 2545 Datasheet,Nylon 6,Honeywell-SHANGHAI SUSHENG

Message
OxyShield®2545 is a polyamide 6 (nylon 6) product,. It is available in North America. OxyShield®2545 application areas include packaging and movies. Features include: high gloss high strength

General Information
Features	Highlight High strength
Uses	Bi-axially Oriented Film Packaging
Forms	Films

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D955
Flow	1.3 - 2.0	%	ASTM D955
Transverse flow	0.0 - 0.50	%	ASTM D955

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.27	ASTM D1894
With self-dynamics	0.78	ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	28	µm
secant modulus			ASTM D882
MD	2840	MPa	ASTM D882
TD	2840	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Fracture	248	MPa	ASTM D882
TD : Fracture	248	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	90	%	ASTM D882
TD : Fracture	90	%	ASTM D882
Elmendorf Tear Strength			ASTM D1922
MD	19	g	ASTM D1922
TD	19	g	ASTM D1922
Oxygen Permeability (23°C, 65% RH)	0.21	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission	9.3	g/m²/24 hr	ASTM E96

Optical	Nominal Value	Unit	Test Method
Gloss (20°)	80		ASTM D2457
Haze	5.0	%	ASTM D1003

Additional Information
Tensile Strength @ Break, ASTM D 882, MD & TD: 30000 - 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 - 110%Secant Modulus, ASTM D 882, MD & TD: 350000 - 475000 psiElmendorf Tear Str, ASTM D 1922, MD & TD: 15 - 19 g/milGraves Tear (initial), ASTM D 1004: 1100 - 1400 g/milGloss (20°), ASTM D 2457: 75 - 85Coefficient of Friction, ASTM D 1894: 0.65 - 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.24 - 0.30 vs Metal-DynamicOxygen Permeability, ASTM D 3985, 73°F/0% RH: .52 cc/100 in²/dayThe value listed as Mold Shrink, Linear-Flow, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Mold Shrink, Linear-Trans, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Water Vapor Transmission , ASTM E 96, was tested in accordance with ASTM F 1249.

Additional Information

Tensile Strength @ Break, ASTM D 882, MD & TD: 30000 - 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 - 110%Secant Modulus, ASTM D 882, MD & TD: 350000 - 475000 psiElmendorf Tear Str, ASTM D 1922, MD & TD: 15 - 19 g/milGraves Tear (initial), ASTM D 1004: 1100 - 1400 g/milGloss (20°), ASTM D 2457: 75 - 85Coefficient of Friction, ASTM D 1894: 0.65 - 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.24 - 0.30 vs Metal-DynamicOxygen Permeability, ASTM D 3985, 73°F/0% RH: .52 cc/100 in²/dayThe value listed as Mold Shrink, Linear-Flow, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Mold Shrink, Linear-Trans, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Water Vapor Transmission , ASTM E 96, was tested in accordance with ASTM F 1249.

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	OxyShield®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HNLsW1_OxyShield-2545.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
PRIME TPO F-3910	Prime Polymer Co., Ltd.	PP Random Copolymer	PRIME TPO
megol® EUG 40	API SpA	SEBS	megol®
ACCUTECH™ CP0437C10L1	ACLO Compounders Inc.	PP Copolymer	ACCUTECH™
DENIFORM 2510	Vamp Tech	Acetal (POM) Copolymer	DENIFORM
KRATON® D1192 E	Kraton Polymers LLC	SBS	KRATON®