EPO-TEK® 310T-M
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HN8hXq_EPO-TEK-310T-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, flexible epoxy designed for low stress applications in semiconductor, hybrid, medical, acoustical and optical industries. Replacement for EPO-TEK® 310T. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 401 | °C | |
| Die Shear Strength - >3 kg (23°C) | 7.03 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 8.43 | MPa | |
| Thixotropic Index | 2.10 | ||
| Weight Loss on Heating | |||
| 200°C | 0.050 | % | |
| 250°C | 0.18 | % | |
| 300°C | 0.63 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | < 30.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 7.4E-5 | cm/cm/°C | |
| -- 3 | 2.4E-4 | cm/cm/°C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 6.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Clear/Transparent | ||
| -- 5 | Tan | ||
| Density | |||
| Part B | 1.08 | g/cm³ | |
| Part A | 1.12 | g/cm³ | |
| Viscosity 6(23°C) | 1.8 to 3.3 | Pa·s | |
| Curing Time (65°C) | 2.0 | hr | |
| Pot Life | 35 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 75 | ||
| Lap Shear Strength (23°C) | 3.45 | MPa | |
| Relative Permittivity (1 kHz) | 5.10 | ||
| Volume Resistivity (23°C) | > 2.5E+10 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.091 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terlux® 2802 | INEOS Styrolution Group GmbH | MABS | Terlux® |
| ALTECH® PA66 A 2015/109 GF15 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| BP ABS 3333 R BLK | Buckeye Polymers, Inc. | ABS | BP |
| Karina BLACK PVC COMPOUND 751D48/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen 4261 AG BD | LyondellBasell Industries | HDPE, HMW | Lupolen |