POLYLAC® PA-777C
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HN2D5K_POLYLACPA777C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High heat, High impact |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 44.0 | MPa | ISO 527-2/50 |
| Fracture | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 44 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | ISO 180/1A |
| 23°C | 18 | kJ/m² | ISO 180/1A |
| Drop Impact Resistance | ASTM D4226 | ||
| -30°C | 9.00 | J/cm | ASTM D4226 |
| 23°C | 17.0 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, not annealed | 92.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 112 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 119 | °C | ISO 306/A50 |
| -- | 112 | °C | ISO 306/B50 |
| CLTE - Flow | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 332E FR | RTP Company | PC | RTP |
| Thermx® LED 0201S | Celanese Corporation | PCT | Thermx® |
| Badamid® LB75 K | Bada AG | Nylon 6 | Badamid® |
| Daplen™ EG251AIB | Borealis AG | TPO | Daplen™ |
| Keltan® 9950C | LANXESS Buna GmbH | EPDM | Keltan® |