HiFill® PET GF55 2000
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HN1Ev1_HiFill-PET-GF55-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PET GF55 2000 is a Polyethylene Terephthalate (PET) product filled with 55% glass fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 193 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 17200 | MPa | ASTM D790 |
| Flexural Strength | 303 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 229 | °C | ASTM D648 |
| Melting Temperature | 254 | °C | |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 271 to 288 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 271 to 288 | °C | |
| Processing (Melt) Temp | 274 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF2704 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Chiao Fu PA6 MC312G20 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| ELASTOSIL® R plus 4020/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Karina IVORY PVC COMPOUND 105908-35/ 1-BY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST XU 6100BB02 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |