Plenco 01510 (Injection)
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HMtkmG_Plenco-01510-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 01510 is a mineral filled, pelletized polyester molding compound, which offers an excellent combination of electrical properties and dimensional stability. UL recognized under component file E40654. 01510 is available in black. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.02 | g/cm³ | ASTM D792 |
| Apparent Density | 0.96 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.38 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 72 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20900 | MPa | ASTM D638 |
| Tensile Strength | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 19100 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Compressive Strength | 155 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 22.8 | J/m | ASTM D256 |
| Notched Izod Impact | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 249 | °C | ASTM D648 |
| Continuous Use Temperature | 215 | °C | ASTM D794 |
| CLTE - Flow | 4.8E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.6E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 15 | kV/mm | ASTM D149 |
| -- 2 | 12 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.016 | ASTM D150 | |
| Arc Resistance | 191 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.00%Heat Resistance, ASTM D794: 215°CDrop Ball Impact, PLENCO Method: 128 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 49.0 - 71.0 | °C | |
| Front Temperature | 85.0 - 93.0 | °C | |
| Processing (Melt) Temp | 93.0 - 100 | °C | |
| Mold Temperature | 163 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-6 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Haprez™ 3744 | Hapco Inc. | TP, Unspecified | Haprez™ |
| INELEC ABSCF20 | Infinity LTL Engineered Compounds | ABS | INELEC |
| Kuraray R-Polymer R-3109 | Kuraray Co., Ltd. | PVOH | Kuraray R-Polymer |
| Jam PE 16503 | Jam Petrochemical Company | LLDPE | Jam PE |
| LNP™ LUBRICOMP™ Cycoloy_C6303 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |