Bayflex® 190 RRIM (20% Mica)
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HLWITe_Bayflex-190-RRIM-20-Mica-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bayflex 190 is an ELPO (electrophoresis-capable) high-performance polyurea with excellent heat stability, low moisture absorption, low thermal expansion characteristics, and excellent impact resistance. Parts made from this material have superior surface and paint adhesion qualities and have a DOI (Distinction of Image) comparable to painted steel parts. The Bayflex 190 system is an excellent choice for applications such as truck fenders and tailgates. As with any product, use of the Bayflex 190 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. Bayflex 190 is a formulated RIM system, supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer and Component B is a polyether amine system. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D1622, ASTM D792 |
| Molding Shrinkage - Flow | 0.75 | % | Internal method |
| Water absorption- 240 hr (3.81 mm) | 0.10 | % | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Impact (3.81 mm) 1 | 801 | J/m | Internal method |
| Heat Sag - 6 in Overhang 2 | ASTM D3769 | ||
| 191°C, 3.81 mm | 4.50 | mm | ASTM D3769 |
| 250°C, 3.81 mm | 0.500 | mm | ASTM D3769 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 3.81 mm) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.81 mm) | 15 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -30°C, 3.81 mm | 2590 | MPa | ASTM D790 |
| 23°C, 3.81 mm | 1720 | MPa | ASTM D790 |
| 65°C, 3.81 mm | 1030 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 3.81 mm) | 37.9 | MPa | ASTM D412 |
| Tensile Elongation (Break, 3.81 mm) | 15 | % | ASTM D412 |
| Tear Strength 3(3.81 mm) | 123 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (3.81 mm) | 7.1E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components 4 | |||
| Component a | Mixing ratio by weight: 120 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Part A Type: Isocyanate Appearance: Colorless to light yellow liquid Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 600 mPa-s Flash Point PMCC: 220 °C Part B Type: Polyol Appearance: Yellow to amber liquid Specific Gravity @ 25°C: 1.02 Viscosity @25°C: 800 mPa-s Flash Point PMCC: 171 °C Molding Parameters Material Temperature - Component A: 27 to 49 °C Material Temperature - Component B: 46 to 60 °C Mold Temperature: 74 to 85 °C shot time: 1.0 to 1.2 sec sec |
| Note Message | |
|---|---|
| 1 . | 5 mph |
| 2 . | 1 hr |
| 3 . | C mould |
| 4 . | 105 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3X2G5 BK23187 | BASF Corporation | Nylon 66 | Ultramid® |
| Exelene® PP H0901 | Montachem International, Inc. | PP Homopolymer | Exelene® PP |
| Generic Nylon 66 - Mineral | Generic | Nylon 66 | Generic |
| omay® G32 | Suzhou OMAY Optical Materials Co., Ltd | Film, PC | omay® |
| Pro-fax PL395N | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |