Propafilm™ RXL80
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HLSP3R_Propafilm-RXL80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
One Side High Barrier PVdC Coated Lamination Film Biaxially oriented polypropylene (BOPP) film coated on one side with an aqueous dispersion of polyvinylidene chloride (PVdC) copolymer. The other surface is a discharge treated coextruded layer. RXL80 is suitable for use in lamination structures especially for dried foods, snacks and general barrier lamination applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 120°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 1 | 0.50 to 0.60 | ||
| vs. Itself - Dynamic, PVdC/PVdC | 0.30 to 0.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 2000 | µm | |
| Seal Strength 2 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature | |||
| -- 3 | 104 to 146 | °C | |
| -- 4 | 129 to 146 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 0.15 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 4.0 | g/m²/24 hr | ASTM F1770 |
| Yield | 52.3 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 100 | ASTM D2457 | |
| Haze 5 | 2.0 to 3.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Coextruded/Coextruded |
| 2 . | PVdC/PVdC; 2secs; 15psi |
| 3 . | PVdC/PVdC; 2secs; 15psi |
| 4 . | Coextruded/Coextruded; 2secs; 15psi |
| 5 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PA523G15 | Guangdong Silver Age Sci & Tech. Co., Ltd | Nylon 6 | SILVER® |
| DOMAMID® 6GM304 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Karina BLUE PVC COMPOUND 650-06/127 (MP-1.0) (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina ORANGE PVC COMPOUD 905-32/170-CY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Rotuba CAB B9004 (10% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |