Larpeek 10 GCE/600
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larpeek |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HKEImg_Larpeek-10-GCE-600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyetheretherketone (PEEK). UL94 V-0 classified, halogens free. Glass fibres / Mineral filler. Very good chemical resistance. Very good thermal resistance. Low smoke toxicity index and optical density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.93 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.30 to 0.50 | % | |
| Flow : 2.00 mm | 0.20 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 17500 | MPa | |
| 60°C | 17000 | MPa | |
| 90°C | 17000 | MPa | |
| 120°C | 16000 | MPa | |
| 150°C | 15500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 160 | MPa | |
| Break, 60°C | 145 | MPa | |
| Break, 90°C | 135 | MPa | |
| Break, 120°C | 115 | MPa | |
| Break, 150°C | 100 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.3 | % | |
| Break, 60°C | 1.3 | % | |
| Break, 90°C | 1.4 | % | |
| Break, 120°C | 1.4 | % | |
| Break, 150°C | 1.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 300 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 300 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 250 | °C | |
| Vicat Softening Temperature | > 300 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 390 to 400 | °C | |
| Mold Temperature | 170 to 200 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 C TFE 15 | RTP Company | PPS | RTP |
| PRIMALENE WPP513ED05 | Southern Polymer, Inc. | EVA | PRIMALENE |
| Nypol® PA B3 G15 NTLA010 NT317 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Beetle® PBTS100 | Teknor Apex Company (Chem Polymer) | PBT | Beetle® |
| Karina BLACK PVC COMPOUND -E 805D48/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |