Order Products : sales@su-jiao.com
Chemlon® MD82
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HK9CQV_Chemlon-MD82.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MD82 is a UL recognised, V-0 rated, halogen & phosphorus free flame retardant, unreinforced injection moulding grade of nylon 6. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.1 - 1.5 | -- | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2900 | 2300 | MPa | ISO 527-2 |
| Tensile Stress | 70.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 3100 | 1500 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 85.0 | 35.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | > 100 | > 100 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 9.0 | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 3.0 | -- | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | No Break | -- | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | 75.0 | °C | ISO 75-2/A |
| CLTE - Flow | 6.0E-5 | -- | cm/cm/°C | Internal method |
| Thermal Conductivity | 0.34 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 15 | 12 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 4.00 | 4.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | > 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.630 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.00 mm | 960 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 36 | -- | % | ISO 4589-2 |
| Additional Information |
|---|
| 干燥 Due to the thermal sensitivity of flame retarded products steps should be taken to limit hold up time and temperature for the material. Additional care should be taken during any interruptions to routine production and during any purging procedures in order to minimise degradation of the product. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 240 - 250 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | Low | ||
| Screw Speed | Moderate |
| Injection instructions |
|---|
| No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® HHM TR-257 | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| TOYOBO Urethane E1095A | TOYOBO America, Inc. | PUR-Butyl | TOYOBO Urethane |
| Nypol® PA A3 G20 V10 PRTA010 NR302 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Sylvin 8215-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Plexar® PX1140 | LyondellBasell Industries | PE, Unspecified | Plexar® |