Purell PE 3020 H
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Purell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HK6DwB_Purell-PE-3020-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Purell PE 3020 H is a high purity low density polyethylene with high rigidity, good opticals and good chemical resistance. It is delivered in pellet form. The grade is used by our customers for films and extrusion coating for healthcare applications including primary and secondary packaging of pharmaceuticals. Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical (P & AD) and Business contacts first. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 51 | ISO 868 | |
| Ball Indentation Hardness (H 49/30) | 21.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 13.0 | MPa | ISO 527-2 |
| Coefficient of Friction | 0.55 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 20 to 60 µm | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, blown film | 18.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 350 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 110 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 114 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | 110 | ASTM D2457 | |
| 60, 50.0 µm, blown film | 70 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 6.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy | 40.0 | J/cm | DIN 53373 |
| Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 180°C and a blow-up ratio of 2:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV350 | Radici Plastics | Nylon 66 | Radilon® |
| ResMart Ultra HDPE 20 | ResMart | HDPE | ResMart Ultra |
| STARFLEX® P 7393-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| NOVAPOL® TD-9022 Series | NOVA Chemicals | LLDPE | NOVAPOL® |
| Caltex PP 5850Y | GS Caltex | PP Random Copolymer | Caltex PP |