Niretan B SV20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HK2HWV_Niretan-B-SV20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Niretan B SV20 is a Polyamide 6 (Nylon 6) material filled with 20% glass bead. It is available in Europe for injection molding. Primary attribute of Niretan B SV20: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.25 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 1.4 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 8.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.7 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | |||
| Yield | 65.0 | 45.0 | MPa | |
| Break | 65.0 | 45.0 | MPa | |
| Tensile Elongation 2(Break) | 4.0 | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 3800 | 1300 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 90.0 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 40 | 50 | J/m | |
| 23°C, 3.20 mm | 60 | 80 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 30 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP2B40 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Pro-fax RP320N | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| RTP EMI 1363 | RTP Company | PPS | RTP |
| Bergamid™ A700 G30 H RED 3000 (F1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Halene L 71602W | Haldia Petrochemicals Ltd. | LLDPE | Halene L |