| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HIpUBi_SABICHDPEB5206.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B5206 is a material with a semi-high molecular mass, typically used for blow moulding of UN certified cans and containers in the range from 10 to 120 liters. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 6.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.28 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1100 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 25.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 38.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 14 | % | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1050 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 25.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 29.0 | MPa | ISO 18488 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 180 | J/g | ISO 11357-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C, molded | 22 | kJ/m² | ISO 180/A |
| 23°C, molded | 40 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 77.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 FR NH | RTP Company | Nylon 66 | RTP |
| VICOTE® 701 | Victrex plc | PEEK | VICOTE® |
| Nanjing Hongrui PA6 B500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| Next Nylon 66 Prime Series PG40-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| GELOY™ XP7560 resin | SABIC Innovative Plastics Europe | ASA | GELOY™ |